| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.15 g/cc | 1.15 g/cc | ASTM D792 |
| 密度 | 1.15 g/cc | 0.0415 lb/in³ | ISO 1183 |
| Water Absorption | 5.0 %
@Temperature 23.0 °C
|
5.0 %
@Temperature 73.4 °F
|
Immersion 24h; ASTM D570 |
| 5.0 %
@Temperature 23.0 °C
|
5.0 %
@Temperature 73.4 °F
|
Immersion 24h; ISO 62 | |
| 线性成型收缩率 | 0.0050 cm/cm | 0.0050 in/in | Flow; ASTM D955 |
| 线性成型收缩率,Flow | 0.010 cm/cm
@Thickness 2.00 mm
|
0.010 in/in
@Thickness 0.0787 in
|
ISO 294-4 |
| 线性成型收缩率，横向 | 0.010 cm/cm
@Thickness 2.00 mm
|
0.010 in/in
@Thickness 0.0787 in
|
ISO 294-4 |
| 熔体流动速率 | 10 g/10 min
@Load 2.16 kg, Temperature 190 °C
|
10 g/10 min
@Load 4.76 lb, Temperature 374 °F
|
ASTM D1238 |
| 10 g/10 min
@Load 2.16 kg, Temperature 190 °C
|
10 g/10 min
@Load 4.76 lb, Temperature 374 °F
|
ISO 1133 |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 肖氏硬度 (邵氏 D) | <= 35 | <= 35 | ASTM D2240 |
| <= 35 | <= 35 | ISO 868 | |
| 26
@Time 15.0 sec
|
26
@Time 0.00417 hour
|
ISO 868 | |
| 抗张强度(断裂) | 9.70 MPa
@Temperature 23.0 °C
|
1410 psi
@Temperature 73.4 °F
|
ISO 527 (1BA bar) |
| 10.3 MPa
@Temperature 23.0 °C
|
1490 psi
@Temperature 73.4 °F
|
ASTM D638 | |
| 抗张强度 | 1.70 MPa
@Strain 5.00 %, Temperature 23.0 °C
|
247 psi
@Strain 5.00 %, Temperature 73.4 °F
|
ASTM D638 |
| 2.50 MPa
@Strain 10.0 %, Temperature 23.0 °C
|
363 psi
@Strain 10.0 %, Temperature 73.4 °F
|
ISO 527 (1BA bar) | |
| 2.60 MPa
@Strain 10.0 %, Temperature 23.0 °C
|
377 psi
@Strain 10.0 %, Temperature 73.4 °F
|
ASTM D638 | |
| 伸长率 (断裂) | 200 %
@Temperature 23.0 °C
|
200 %
@Temperature 73.4 °F
|
ASTM D638 |
| 240 %
@Temperature 23.0 °C
|
240 %
@Temperature 73.4 °F
|
ISO 527 (1BA bar) | |
| 拉伸模量 | 0.0230 GPa
@Temperature 23.0 °C
|
3.34 ksi
@Temperature 73.4 °F
|
ISO 527 |
| 弯曲模量 | 0.00700 GPa
@Temperature 100 °C
|
1.02 ksi
@Temperature 212 °F
|
ASTM D790 |
| 0.00700 GPa
@Temperature 100 °C
|
1.02 ksi
@Temperature 212 °F
|
ISO 178 | |
| 0.0320 GPa
@Temperature 23.0 °C
|
4.64 ksi
@Temperature 73.4 °F
|
ISO 178 | |
| 0.0324 GPa
@Temperature 23.0 °C
|
4.70 ksi
@Temperature 73.4 °F
|
ASTM D790 | |
| 0.0500 GPa
@Temperature -40.0 °C
|
7.25 ksi
@Temperature -40.0 °F
|
ISO 178 | |
| 0.0620 GPa
@Temperature -40.0 °C
|
8.99 ksi
@Temperature -40.0 °F
|
ASTM D790 | |
| 悬壁梁缺口冲击强度 | NB
@Temperature -40.0 °C
|
NB
@Temperature -40.0 °F
|
ASTM D256 |
| NB
@Temperature 23.0 °C
|
NB
@Temperature 73.4 °F
|
ASTM D256 | |
| NB
@Temperature -40.0 °C
|
NB
@Temperature -40.0 °F
|
ISO 180/1A | |
| 简支梁缺口冲击强度 | NB
@Temperature -30.0 °C
|
NB
@Temperature -22.0 °F
|
ISO 179/1eA |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 相比耐漏电起痕指数(CTI) | >= 600 V
@Thickness 3.00 mm, Temperature 23.0 °C
|
>= 600 V
@Thickness 0.118 in, Temperature 73.4 °F
|
UL 746A |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 线形热膨胀系数 - 流动 | 500 µm/m-°C
@Temperature -40.0 - 23.0 °C
|
278 µin/in-°F
@Temperature -40.0 - 73.4 °F
|
ASTM E 831 |
| 500 µm/m-°C
@Temperature 23.0 - 55.0 °C
|
278 µin/in-°F
@Temperature 73.4 - 131 °F
|
ASTM E 831 | |
| 500 µm/m-°C
@Temperature -40.0 - 23.0 °C
|
278 µin/in-°F
@Temperature -40.0 - 73.4 °F
|
ISO 11359-1/-2 | |
| 500 µm/m-°C
@Temperature 23.0 - 55.0 °C
|
278 µin/in-°F
@Temperature 73.4 - 131 °F
|
ISO 11359-1/-2 | |
| 线性热膨胀系数,横向流动 | 220 µm/m-°C
@Temperature -40.0 - 23.0 °C
|
122 µin/in-°F
@Temperature -40.0 - 73.4 °F
|
ASTM E 831 |
| 220 µm/m-°C
@Temperature -40.0 - 23.0 °C
|
122 µin/in-°F
@Temperature -40.0 - 73.4 °F
|
ISO 11359-1/-2 | |
| 240 µm/m-°C
@Temperature 23.0 - 55.0 °C
|
133 µin/in-°F
@Temperature 73.4 - 131 °F
|
ASTM E 831 | |
| 240 µm/m-°C
@Temperature 23.0 - 55.0 °C
|
133 µin/in-°F
@Temperature 73.4 - 131 °F
|
ISO 11359-1/-2 | |
| 310 µm/m-°C
@Temperature 55.0 - 120 °C
|
172 µin/in-°F
@Temperature 131 - 248 °F
|
ASTM E 831 | |
| 310 µm/m-°C
@Temperature 55.0 - 120 °C
|
172 µin/in-°F
@Temperature 131 - 248 °F
|
ISO 11359-1/-2 | |
| 熔融温度 | 154 °C | 309 °F | 10°C/min; ISO 11357-1/-3 |
| 156 °C | 313 °F | ASTM D3418 | |
| 脆化温度 | -61.0 °C | -77.8 °F | ISO 974 |
| UL RTI | 50.0 °C
@Thickness 1.50 mm
|
122 °F
@Thickness 0.0591 in
|
UL 746B |
| 50.0 °C
@Thickness 3.00 mm
|
122 °F
@Thickness 0.118 in
|
UL 746B | |
| UL RTI，机械冲击 | 50.0 °C
@Thickness 3.00 mm
|
122 °F
@Thickness 0.118 in
|
UL 746B |
| 50.0 °C
@Thickness 1.50 mm
|
122 °F
@Thickness 0.0591 in
|
UL 746B | |
| UL RTI，机械无冲击 | 50.0 °C
@Thickness 1.50 mm
|
122 °F
@Thickness 0.0591 in
|
UL 746B |
| 50.0 °C
@Thickness 3.00 mm
|
122 °F
@Thickness 0.118 in
|
UL 746B | |
| 可燃性(UL94) | HB
@Thickness 1.50 mm
|
HB
@Thickness 0.0591 in
|
IEC 60695-11-10 |
| HB
@Thickness 3.00 mm
|
HB
@Thickness 0.118 in
|
IEC 60695-11-10 | |
| HB
@Thickness 1.50 mm
|
HB
@Thickness 0.0591 in
|
UL94 | |
| HB
@Thickness 3.00 mm
|
HB
@Thickness 0.118 in
|
UL94 |
| 加工性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 加工（熔体）温度 | 180 °C | 356 °F | Optimum; Extrusion |
| 190 °C | 374 °F | Optimum; Injection Molding | |
| 模具温度 | 30.0 - 40.0 °C | 86.0 - 104 °F | Injection Molding |
| 40.0 °C | 104 °F | optimum; Injection Molding | |
| 干燥温度 | 80.0 °C | 176 °F | Extrusion |
| 80.0 °C | 176 °F | Injection Molding | |
| 干燥时间 | 2.00 - 3.00 hour | 2.00 - 3.00 hour | Extrusion |
| 2.00 - 3.00 hour | 2.00 - 3.00 hour | Injection Molding | |
| 水分含量 | <= 0.080 % | <= 0.080 % | Extrusion |
| <= 0.080 % | <= 0.080 % | Injection Molding |
| 材料描述 | 测试方法 | |
|---|---|---|
| 添加剂 | Antioxidant | |
| 外观 | Beige, Light | |
| Drying Recommended | Yes | |
| Extrudable - Blown Film | Yes | |
| Extrudable - Cast Film | Yes | |
| Extrudable - Coating | Yes | |
| Extrudable - Filament | Yes | |
| Extrudable - Hose | Yes | |
| Extrudable - Sheet | Yes | |
| Extrudable - Tubing | Yes | |
| Extrudable - Wire and Cable | Yes | |
| Extrusion Blow Moldable | Yes | |
| 特性 | Color Stability, Good | |
| Copolymer, Block | ||
| General Purpose | ||
| Hardness, Low | ||
| 形式 | Pellets | |
| Generic | TPC-ET | |
| Heat Stabilized | Yes | |
| Injection Blow Moldable | Yes | |
| Material Status | Current | |
| Melt Castable | Yes |