Tenite™ cellulosic plastics are noted for their excellent balance of properties - toughness, hardness,

strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite™ cellulosic pla

stics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resist

ance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer co

ntent increases impact strength. Tenite™ cellulosic plastics are available in natural, clear, selected a

mbers, or smoke transparents and black translucent. Color concentrates are available in let-down r

atios from 10:1 to 40:1. Tenite™ Cellulose Acetate Butyrate 530-10 contains an odor mask and has a

plasticizer level of 10%.

基本信息
添加剂	增塑剂 (10%)
特性	高光 经增塑 可更新资源 良好的强度 气味低到无 清晰度，高 韧性良好 柔软 硬度高
用途	Decorative Displays 安全设备 把手 家具 镜架 体育用品 玩具 文具 眼镜
外观	黑色 琥珀色 清晰/透明 自然色
形式	粒子

物理性能	额定值	单位制	测试方法
比重	1.19	g/cm³	ASTM D792
收缩率 - 流动	0.20 到 0.60	%	ASTM D955
吸水率 (23°C, 24 hr)	1.4	%	ASTM D570

硬度	额定值	单位制	测试方法
洛氏硬度 (R 级, 23°C)	78		ASTM D785

机械性能	额定值	单位制	测试方法
抗张强度			ASTM D638
屈服, 23°C	33.1	MPa	ASTM D638
断裂, 23°C	43.4	MPa	ASTM D638
伸长率 (断裂, 23°C)	50	%	ASTM D638
弯曲模量 (23°C)	1380	MPa	ASTM D790
弯曲强度 (屈服, 23°C)	45.5	MPa	ASTM D790

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度			ASTM D256
-40°C	96	J/m	ASTM D256
23°C	240	J/m	ASTM D256

热性能	额定值	单位制	测试方法
载荷下热变形温度 1			ASTM D648
0.45 MPa, 退火	85.0	°C	ASTM D648
1.8 MPa, 退火	74.0	°C	ASTM D648
维卡软化温度 2	104	°C	ASTM D1525
线形热膨胀系数 - 流动 (23°C)	2.0E-5	cm/cm/°C	ASTM D696
比热 (23°C)	1260 到 1670	J/kg/°C	DSC
导热系数 3(23°C)	0.25	W/m/K	ASTM C177

电气性能	额定值	单位制	测试方法
介电强度 (23°C)	12 到 19	kV/mm	ASTM D149
介电常数 (23°C, 1 MHz)	3.30 到 3.80		ASTM D150
耗散因数 (23°C, 1 MHz)	0.010 到 0.15		ASTM D150

光学性能	额定值	单位制	测试方法
折射率	1.460 到 1.490		ASTM D542
透射率 (1520 µm)	> 90.0	%	ASTM D1003
雾度 (1520 µm)	< 8.5	%	ASTM D1003

补充信息	额定值	单位制	测试方法
Soluble Matter Loss (23°C)	0.10	%	ASTM D570
Weight Loss on Heating - 72 hrs (80°C)	0.50	%	ASTM D707