Tenite™ cellulosic plastics are noted for their excellent balance of properties - toughness, hardness

, strength, surface gloss, clarity, and a warm feel. The mechanical properties of Tenite™ cellulosic pl

astics differ with plasticizer levels. Lower plasticizer content yields a harder surface, higher heat resi

stance, greater rigidity, higher tensile strength, and better dimensional stability. Higher plasticizer c

ontent increases impact strength. Tenite™ cellulose plastics are available in natural, clear, selected

ambers, or smoke transparents and black translucents. Color concentrates are available in let-dow

n ratios from 10:1 to 40:1. Tenite™ Cellulose Acetate Butyrate 285-20 has a plasticizer level of 20%

and contains an odor mask.

基本信息
添加剂	增塑剂 (20%)
特性	高光 经增塑 可更新资源 良好的强度 气味低到无 清晰度，高 韧性良好 柔软 硬度高
用途	把手 体育用品 玩具
外观	黑色 琥珀色 清晰/透明 自然色
形式	粒子

物理性能	额定值	单位制	测试方法
比重	1.17	g/cm³	ASTM D792
吸水率 (23°C, 24 hr)	1.2	%	ASTM D570

硬度	额定值	单位制	测试方法
洛氏硬度 (R 级, 23°C)	12		ASTM D785

机械性能	额定值	单位制	测试方法
抗张强度			ASTM D638
屈服, 23°C	21.4	MPa	ASTM D638
断裂, 23°C	27.6	MPa	ASTM D638
伸长率 (断裂, 23°C)	50	%	ASTM D638
弯曲模量 (23°C)	965	MPa	ASTM D790
弯曲强度 (屈服, 23°C)	27.6	MPa	ASTM D790

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度			ASTM D256
-40°C	110	J/m	ASTM D256
23°C	380	J/m	ASTM D256

热性能	额定值	单位制	测试方法
载荷下热变形温度 1			ASTM D648
0.45 MPa, 退火	72.0	°C	ASTM D648
1.8 MPa, 退火	58.0	°C	ASTM D648
维卡软化温度 2	92.0	°C	ASTM D1525

补充信息	额定值	单位制	测试方法
Soluble Matter Loss (23°C)	0.10	%	ASTM D570
Weight Loss on Heating - 72 hrs (80°C)	1.0	%	ASTM D707