NEOFLON PFA is a copolymer of tetrafluoroethylene and perfluoroalkyl vinyl ether, NEOFLON PFA is a compound of carbon atoms and fluorine atoms in which a perfluoroalkoxy radical is bonded to the carbon chain in the following molecular structure.

NEOFLON PFA has better mechanical strength at high temperatures than NEOFLON FEP, and has excellent moldability for easy of processing by extrusion, compression, blow, transfer, and injection molding methods. Due to the high bonding strength of the carbon, fluorine and oxygen atoms, NEOFLON PFA demonstrates nearly the same outstanding capabilities as PTFE in temperatures ranging -200°C ~+260°C. NEOFLON PFA has excellent transparency for use in melt-flow processing.

基本信息
特性	低摩擦系数 高温强度 共聚物 良好的成型性能 良好的电气性能 良好的抗腐蚀性 耐气候影响性能良好 清晰度，高 阻燃性
用途	电线护套 涂层应用
外观	半透明 可用颜色
形式	粒子
加工方法	挤出 注射成型

物理性能	额定值	单位制	测试方法
比重	2.14 到 2.16	g/cm³	ASTM D792
表观密度	1.00 到 1.40	g/cm³	JIS K6891
熔流率（熔体流动速率） (372°C/5.0 kg)	10 到 17	g/10 min	ASTM D1238
吸水率 (饱和)	< 0.010	%	ASTM D570

硬度	额定值	单位制	测试方法
肖氏硬度 (邵氏 D)	60 到 70		ASTM D2240

机械性能	额定值	单位制	测试方法
抗张强度 (屈服)	25.4 到 30.4	MPa	JIS K6891
伸长率 (断裂)	350 到 450	%	JIS K6891
弯曲模量	580 到 690	MPa	ASTM D790
压缩模量	490 到 590	MPa	ASTM D695
压缩强度			ASTM D695
1% 应变	4.90 到 5.90	MPa	ASTM D695
25% 应变	31.4 到 33.3	MPa	ASTM D695
摩擦系数 (与钢 - 静态)	0.040 到 0.050
负载变形			ASTM D621
25°C, 14 MPa 1	8.00 到 9.00	%	ASTM D621
25°C, 14 MPa 2	2.50 到 3.00	%	ASTM D621
100°C, 6.9 MPa 3	8.50 到 9.50	%	ASTM D621
100°C, 6.9 MPa 4	2.00 到 3.00	%	ASTM D621
Flexural Strength	No break		ASTM D790

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度	无断裂		ASTM D256

热性能	额定值	单位制	测试方法
熔融温度	300 到 310	°C	ASTM D4591
线形热膨胀系数 - 流动 (20 到 100°C)	1.2E-4	cm/cm/°C	ASTM D696
比热	1050	J/kg/°C
导热系数	0.26	W/m/K	ASTM C177

可燃性	额定值	单位制	测试方法
UL 阻燃等级 (1.57 mm)	V-0		UL 94
极限氧指数 (1.57 mm)	> 95	%	ASTM D2863

充模分析	额定值	单位制
熔体粘度 (380°C)	2.00E+6 到 2.50E+7	mPa·s