GUR® 2122
超高分子量聚乙烯
Celanese Corporation
UHMWPE GUR 2122产品说明:
GUR 2122 UHMW-PE is a linear polyolefin resin in powder form with a molecular weight of approximately 4.5 MM g/mol calculated using Margolies' equation. The extremely high molecular weight of this resin yields several unique properties including superior abrasion resistance and impact strength. Its unique morphology produces a low bulk density (0.20 to 0.25 g/cm3) making this resin particularly suitable for compression molding with high filler content or for free sintering of porous parts.该产品在亚大地区供货商为深圳市仁捷塑胶原料有限公司，销售热线：18681139818，QQ：13931677。
泰科纳超高分子量聚乙烯UHMWPE GUR 2122物性数据：
|
供货地区
|
|
|||
|
特性
|
|
|||
|
RoHS 合规性
|
|
|||
|
形式
|
|
|||
|
加工方法
|
|
| 物理性能 |
额定值
|
单位制
|
测试方法
|
|
比重
|
|||
|
--
|
0.928
|
g/cm³
|
ASTM D792 |
|
--
|
0.930
|
g/cm³
|
ISO 1183 |
|
熔流率（熔体流动速率）
|
|||
|
190°C/21.6 kg
|
< 0.10
|
g/10 min
|
ASTM D1238 |
|
190°C/21.6 kg
|
< 1.0
|
g/10 min
|
ISO 1133 |
|
吸水率
|
ISO 62 | ||
|
饱和, 23°C
|
< 0.010
|
%
|
|
|
平衡, 23°C, 50% RH
|
< 0.010
|
%
|
|
|
粘数
|
2200
|
cm³/g
|
ISO 307 |
|
Elongational Stress F - 150/10
|
0.220
|
MPa
|
ISO 1152-2 |
|
固有粘度
|
20
|
dl/g
|
ISO 1628-3 |
| 硬度 |
额定值
|
单位制
|
测试方法
|
|
肖氏硬度
|
|||
|
邵氏 D
|
63
|
|
ASTM D2240 |
|
邵氏 D, 15 秒
|
60
|
|
ISO 868 |
|
球压硬度 2
|
38.0
|
MPa
|
ISO 2039-1 |
| 机械性能 |
额定值
|
单位制
|
测试方法
|
|
拉伸模量
|
|||
|
23°C
|
703
|
MPa
|
ASTM D638 |
|
--
|
790
|
MPa
|
ISO 527-2/1A/1 |
|
抗张强度
|
|||
|
屈服, 23°C
|
21.4
|
MPa
|
ASTM D638 |
|
屈服
|
17.0
|
MPa
|
ISO 527-2/1A/50 |
|
伸长率
|
|||
|
屈服, 23°C
|
> 350
|
%
|
ASTM D638 |
|
屈服
|
20
|
%
|
ISO 527-2/1A/50 |
|
标称拉伸断裂应变
|
> 50
|
%
|
ISO 527-2/1A/50 |
|
拉伸蠕变模量
|
ISO 899-1 | ||
|
1 hr
|
550
|
MPa
|
|
|
1000 hr
|
270
|
MPa
|
|
|
摩擦系数 (与钢 - 动态)
|
0.10
|
|
内部方法 |
|
磨损量
|
100
|
|
内部方法 |
| 冲击性能 |
额定值
|
单位制
|
测试方法
|
|
Charpy Impact Strength 3
|
120
|
kJ/m²
|
ISO 1152-2 |
| 热性能 |
额定值
|
单位制
|
测试方法
|
|
热变形温度
|
|||
|
0.45 MPa, 未退火
|
65.0
|
°C
|
ISO 75-2/B |
|
1.8 MPa, 未退火
|
42.0
|
°C
|
ISO 75-2/A |
|
维卡软化温度
|
80.0
|
°C
|
ASTM D1525, ISO 306/B50 |
|
线形热膨胀系数 - 流动
|
2.0E-4
|
cm/cm/°C
|
ASTM D696, ISO 11359-2 |
|
比热
|
内部方法 | ||
|
--
|
1840
|
J/kg/°C
|
|
|
23°C
|
1840
|
J/kg/°C
|
|
|
导热系数 (23°C)
|
0.41
|
W/m/K
|
内部方法 |
| 电气性能 |
额定值
|
单位制
|
测试方法
|
|
表面电阻率
|
|||
|
--
|
> 1.0E+13
|
ohm
|
ASTM D257 |
|
--
|
> 1.0E+12
|
ohm
|
IEC 60093 |
|
体积电阻率
|
|||
|
--
|
> 1.0E+15
|
ohm·cm
|
ASTM D257 |
|
--
|
> 1.0E+14
|
ohm·cm
|
IEC 60093 |
|
介电强度
|
45
|
kV/mm
|
IEC 60243-1 |
|
介电常数
|
|||
|
1 MHz
|
3.00
|
|
ASTM D150, IEC 60250 |
|
100 Hz
|
2.10
|
|
IEC 60250 |
|
耗散因数
|
IEC 60250 | ||
|
100 Hz
|
3.9E-4
|
|
|
|
1 MHz
|
1.0E-3
|
|
|
|
漏电起痕指数
|
600
|
V
|
IEC 60112 |
| 可燃性 |
额定值
|
单位制
|
测试方法
|
|
UL 阻燃等级 (1.60 mm)
|
HB
|
|
UL 94 |
| 备注 |
| 1通过这些链接您能够访问供应商资料。我们尽量保证及时更新资料；不过您可以从供应商处了解最新资料。 |
| 230 sec |
| 314° V-notch both sides |
亲，如果要PDF物性表，可以到物性下载栏目下载，或发邮件到：tjh@rjplastics.com索取！
温馨提示：仁捷公司免费24小时提供塑胶原料注塑成型技术支持,咨询热线：18681139818，联系人：唐生
Tag: 超高分子量聚乙烯 ,超高分子量PE ,UHMWPE