Production-Grade Thermoplastic for Fortus 3D Production Systems

PC-ABS (polycarbonate-ABS) is one of the most widely used industrial thermoplastics. PC-A

BS offers the most desirable properties of both materials - the superior strength and heat re

sistance of PC and the flexibility of ABS. PC-ABS blends are commonly used in automotive, e

lectronics and telecommunications applications. Additionally, a PC-ABS part manufactured

on a Fortus® 3D Production System is 5-60 percent stronger than a part made on previous F

DM® systems. When combined with a Fortus system, PC-ABS gives you Real Parts™ concept

ual modeling, functional prototyping, manufacturing tools, and end-use-parts.

基本信息
特性	好的消毒性 抗撞击性，高 良好的强度 良好的柔韧性 耐化学性良好 耐热性，高 耐用性
用途	成型 电气/电子应用领域 工程配件 工业应用 模具 汽车领域的应用 通讯器材
UL文件号	E345258
外观	黑色
加工方法	3D Printing, Fused Filament Fabrication (FFF)

物理性能	额定值	单位制	测试方法
比重	1.10	g/cm³	ASTM D792
Thickness - Layer Capability	127.0 到 330.2	µm

电气性能	额定值	单位制	测试方法
Volume Resistance 1	4.4E+13 到 2.0E+14	ohms	ASTM D257

硬度	额定值	单位制	测试方法
洛氏硬度 (R 级)	110		ASTM D785

机械性能	额定值	单位制	测试方法
拉伸模量 2(3.18 mm)	1920	MPa	ASTM D638
抗张强度 3(3.18 mm)	40.7	MPa	ASTM D638
伸长率 4(断裂, 3.18 mm)	6.0	%	ASTM D638
弯曲模量 5	1930	MPa	ASTM D790
弯曲强度 6	67.6	MPa	ASTM D790

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度 (23°C)	200	J/m	ASTM D256A
无缺口悬臂梁冲击 (23°C)	480	J/m	ASTM D256

热性能	额定值	单位制	测试方法
载荷下热变形温度			ASTM D648
0.45 MPa, 未退火	110	°C	ASTM D648
1.8 MPa, 未退火	96.1	°C	ASTM D648
玻璃转化温度	125	°C	DMA
维卡软化温度	112	°C	ASTM D1525
线形热膨胀系数 - 流动	7.4E-5	cm/cm/°C

电气性能	额定值	单位制	测试方法
介电强度	3.5 到 13	kV/mm	ASTM D149
介电常数 7	2.70 到 2.90		ASTM D150
耗散因数 8	3.2E-3 到 3.5E-3		ASTM D150

可燃性	额定值	单位制	测试方法
UL 阻燃等级	HB		UL 94