Shanghai Ofluorine PVDF J-2

聚偏二氟乙烯

Shanghai Ofluorine Chemical Technology Co., Ltd

产品说明：

Medium melt viscosity, more suitable for extrusion molding.
J-2 PVDF as raw materials, the finished products has excellent mechanical strength and flexi

bility. It can not be eroded by acid, alkali, strong oxidant, halogens. Good durability to aliph

atic hydrocarbons, aromatic hydrocarbons, alcohol, aldehyde etc. In the work of hydrochlori

c acid, nitric acid, sulfuric acid, dilute alkali liquor, dense alkali liquor(40%) and 100deg.C, wh

ich keep stable.
Others, J-2 PVDF finished products has the properties of gamma-Ray resistant, UV resistant, a

nd stability in wide temperature range.
Application: Be used in manufacturing PVDF tubes, PVDF pipes, PVDF rod etc.

基本信息
特性	高强度 抗伽马辐射 抗氧化 抗紫外线性能良好 良好的柔韧性 耐碱 耐酒精 耐酸 耐碳氢化合物 气味低到无 热稳定性，良好 中等粘性
用途	棒材 管道系统 管件
外观	半透明
形式	粒子
加工方法	挤出

物理性能	额定值	单位制	测试方法
比重	1.77 到 1.79	g/cm³	ASTM D792
熔流率（熔体流动速率） (230°C/12.5 kg)	10 到 25	g/10 min	ASTM D1238
吸水率 (平衡)	< 0.050	%	ASTM D570

硬度	额定值	单位制	测试方法
肖氏硬度 (邵氏 D)	70 到 80		ASTM D2240

机械性能	额定值	单位制	测试方法
抗张强度 1			ASTM D638
屈服, 23°C	> 40.0	MPa	ASTM D638
断裂, 23°C	> 30.0	MPa	ASTM D638
伸长率 2			ASTM D638
屈服, 23°C	5.0 到 10	%	ASTM D638
断裂, 23°C	> 50	%	ASTM D638

热性能	额定值	单位制	测试方法
熔融峰值温度 3	165 到 171	°C	ASTM D3418

可燃性	额定值		测试方法
UL 阻燃等级	V-0		UL 94