SABIC Innovative Plastics NORYL N225X PPE+PS
Polymer,Thermoplastic,Polyphenylene Ether/PPO,Polystyrene (PS)
SABIC Innovative Plastics (GE Plastics)
PDF物性文档下载
产品说明:
PPE+PS blend. Unfilled. Halogen-Free FR performance. UL94 V0/5VA. UL746C F1. Dielectric Strength. Suitable for E/E market indoor/outdoor applications.
SABIC Innovative Plastics NORYL N225X PPE+PS 物性表
| 物理性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 比重 | 1.11 g/cc | 1.11 g/cc | ASTM D792 |
| 线性成型收缩率,Flow | 0.0050 - 0.0070 cm/cm
@Thickness 3.20 mm
|
0.0050 - 0.0070 in/in
@Thickness 0.126 in
|
SABIC Method |
| 线性成型收缩率，横向 | 0.0050 - 0.0070 cm/cm
@Thickness 3.20 mm
|
0.0050 - 0.0070 in/in
@Thickness 0.126 in
|
SABIC Method |
| 机械性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 抗张强度(断裂) | 49.0 MPa | 7110 psi | Type I, 50 mm/min; ASTM D638 |
| 抗张强度(屈服) | 66.0 MPa | 9570 psi | Type I, 50 mm/min; ASTM D638 |
| 伸长率 (断裂) | 17 % | 17 % | Type I, 50 mm/min; ASTM D638 |
| 屈服伸长率 | 8.0 % | 8.0 % | Type I, 50 mm/min; ASTM D638 |
| 弯曲强度 | 99.0 MPa | 14400 psi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 弯曲模量 | 2.49 GPa | 361 ksi | 2.6 mm/min, 100 mm span; ASTM D790 |
| 悬壁梁缺口冲击强度 | 1.86 J/cm | 3.48 ft-lb/in | ASTM D256 |
| 0.960 J/cm
@Temperature -30.0 °C
|
1.80 ft-lb/in
@Temperature -22.0 °F
|
ASTM D256 | |
| 8.86 J/cm
@Thickness 3.20 mm
|
16.6 ft-lb/in
@Thickness 0.126 in
|
ASTM D256 | |
| 落锤总能量 | 39.0 J | 28.8 ft-lb | Instrumented Impact Energy @ peak; ASTM D3763 |
| 11.0 J
@Temperature -30.0 °C
|
8.11 ft-lb
@Temperature -22.0 °F
|
Instrumented Impact Energy @ peak; ASTM D3763 |
| 电气性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 体积电阻率 | 2.80e+16 ohm-cm | 2.80e+16 ohm-cm | ASTM D257 |
| 表面电阻 | >= 1.00e+14 ohm | >= 1.00e+14 ohm | ASTM D257 |
| 介电常数 | 2.55
@Frequency 1.00e+6 Hz
|
2.55
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| 2.69
@Frequency 50.0 - 60.0 Hz
|
2.69
@Frequency 50.0 - 60.0 Hz
|
ASTM D150 | |
| 介电强度 | 16.2 kV/mm
@Thickness 3.20 mm
|
411 kV/in
@Thickness 0.126 in
|
in oil; ASTM D149 |
| 耗散因数 | 0.0070
@Frequency 1.00e+6 Hz
|
0.0070
@Frequency 1.00e+6 Hz
|
ASTM D150 |
| 0.010
@Frequency 50.0 - 60.0 Hz
|
0.010
@Frequency 50.0 - 60.0 Hz
|
ASTM D150 | |
| 耐电弧性 | 60 - 120 sec | 60 - 120 sec | Tungsten; ASTM D495 |
| 相比耐漏电起痕指数(CTI) | 400 - 600 V | 400 - 600 V | UL 746A |
| 热丝引燃 (HWI) | 60 - 120 sec | 60 - 120 sec | UL 746A |
| 高电弧燃烧，HAI | >= 120 arcs | >= 120 arcs | UL 746A |
| 高压电弧跟踪率，HVTR | >= 150 mm/min | >= 5.91 in/min | UL 746A |
| 热性能 | 额定值 (公制) | 额定值 (英制) | 测试方法 |
|---|---|---|---|
| 载荷下热变形温度(0.46 MPa) | 109 °C
@Thickness 6.40 mm
|
228 °F
@Thickness 0.252 in
|
unannealed; ASTM D648 |
| 载荷下热变形温度(1.8 MPa) | 99.0 °C
@Thickness 6.40 mm
|
210 °F
@Thickness 0.252 in
|
unannealed; ASTM D648 |
| 维卡软化温度 | 128 °C | 262 °F | Rate B/50; ASTM D1525 |
| UL RTI | 95.0 °C | 203 °F | UL 746B |
| UL RTI，机械冲击 | 80.0 °C | 176 °F | UL 746B |
| UL RTI，机械无冲击 | 95.0 °C | 203 °F | UL 746B |
| 可燃性(UL94) | HB
@Thickness 0.400 mm
|
HB
@Thickness 0.0157 in
|
UL 94 |
| V-0
@Thickness 1.47 mm
|
V-0
@Thickness 0.0579 in
|
UL 94 | |
| 5VA
@Thickness 2.99 mm
|
5VA
@Thickness 0.118 in
|
UL 94 |
| 材料描述 | 测试方法 | |
|---|---|---|
| Radiant Panel Listing | YES | UL Tested |
| UV-light, water exposure/immersion | F1 | UL 746C |