PARYLS® PES F2250GL20 pellets are supplied in cartons lining aluminum foil bag, which can

be stored indefinitely, provided the packaging remains undamaged.
PARYLS® PES F2250GL20 pellets absorb moisture very rapidly. Therefore, the pellets need to

be dried at least 6h at 180 °C in a vacuum or dry air drier prior to processing.

Features
PARYLS® PES F2250GL20, resin is a 20% glass fiber reinforced polysulfone(PSU). Glass fiber s

ubstantially increasee the rigidity, tensile strength, creep resistance, dimensional stability and

chemical resistance of the polysulfone resin. The high performance properties make these re

sins particularly effective alternatives to metals in many engineering applications.

基本信息
填料/增强材料	玻璃纤维增强材料, 20% 填料按重量
特性	尺寸稳定性良好 刚性，高 高强度 良好的抗蠕变性 耐化学性良好
外观	黑色 灰色 自然色
形式	粒子
加工方法	挤出 注射成型

物理性能	额定值	单位制	测试方法
密度	1.50	g/cm³	ISO 1183
熔流率（熔体流动速率） (380°C/2.16 kg)	10 到 15	g/10 min	ISO 1133
收缩率			ISO 294-4, ISO 2577
横向流量	0.61	%	ISO 294-4, ISO 2577
流量	0.36	%	ISO 294-4, ISO 2577
吸水率 (平衡, 23°C, 50% RH)	0.60	%	ISO 62

机械性能	额定值	单位制	测试方法
拉伸模量	7300	MPa	ISO 527-2
拉伸应力	125	MPa	ISO 527-2
拉伸应变 (屈服)	2.5	%	ISO 527-2
弯曲模量	6800	MPa	ISO 178
弯曲应力	150	MPa	ISO 178

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度	6.5	kJ/m²	ISO 180/A

热性能	额定值	单位制	测试方法
热变形温度 (1.8 MPa, 未退火)	220	°C	ISO 75-2/A
玻璃转化温度 1	225	°C	ISO 11357-2, DSC
线形热膨胀系数 - 流动 (23°C)	2.0E-5	cm/cm/°C	ISO 11359-2

电气性能	额定值	单位制	测试方法
表面电阻率 2	> 1.0E+15	ohms	IEC 60093
体积电阻率 3	> 1.0E+15	ohms·cm	IEC 60093
介电强度 4	37	kV/mm	IEC 60243-1
介电常数			IEC 60250
100 Hz	4.20		IEC 60250
1 MHz	4.20		IEC 60250
耗散因数			IEC 60250
100 Hz	2.0E-3		IEC 60250
1 MHz	0.010		IEC 60250
漏电起痕指数	125	V	IEC 60112

可燃性	额定值	单位制	测试方法
UL 阻燃等级 (1.5 mm)	V-0		UL 94

注射	额定值	单位制
干燥温度	180	°C
干燥时间	6.0	hr
加工（熔体）温度	350 到 390	°C
模具温度	140 到 180	°C

挤出	额定值	单位制
干燥温度	180	°C
干燥时间	6.0	hr
熔体温度	350 到 390	°C
口模温度	140 到 180	°C