PARYLS® PES F2250GL30 pellets are supplied in cartons lining aluminum foil bag, which ca

n be stored indefinitely, provided the packaging remains undamaged.
PARYLS® PES F2250GL30 pellets absorb moisture very rapidly. Therefore, the pellets need t

o be dried at least 6h at 180 °C in a vacuum or dry air drier prior to processing.

Features

PARYLS® PES F2250GL30, resin is a 30% glass fiber reinforced polysulfone(PSU). Glass fiber

substantially increasee the rigidity, tensile strength, creep resistance, dimensional stability a

nd chemical resistance of the polysulfone resin. The high performance properties make the

se resins particularly effective alternatives to metals in many engineering applications.

基本信息
填料/增强材料	玻璃纤维增强材料, 30% 填料按重量
特性	尺寸稳定性良好 刚性，高 高强度 良好的抗蠕变性 耐化学性良好
外观	黑色 灰色 自然色
形式	粒子
加工方法	挤出 注射成型

物理性能	额定值	单位制	测试方法
密度	1.60	g/cm³	ISO 1183
熔流率（熔体流动速率） (380°C/2.16 kg)	10 到 15	g/10 min	ISO 1133
收缩率			ISO 294-4, ISO 2577
横向流量	0.58	%	ISO 294-4, ISO 2577
流量	0.25	%	ISO 294-4, ISO 2577
吸水率 (平衡, 23°C, 50% RH)	0.60	%	ISO 62

机械性能	额定值	单位制	测试方法
拉伸模量	10000	MPa	ISO 527-2
拉伸应力	140	MPa	ISO 527-2
拉伸应变 (屈服)	1.9	%	ISO 527-2
弯曲模量	9500	MPa	ISO 178
弯曲应力	160	MPa	ISO 178

冲击性能	额定值	单位制	测试方法
悬壁梁缺口冲击强度	8.0	kJ/m²	ISO 180/A

热性能	额定值	单位制	测试方法
热变形温度 (1.8 MPa, 未退火)	220	°C	ISO 75-2/A
玻璃转化温度 1	225	°C	ISO 11357-2, DSC
线形热膨胀系数 - 流动 (23°C)	1.5E-5	cm/cm/°C	ISO 11359-2

电气性能	额定值	单位制	测试方法
表面电阻率 2	> 1.0E+15	ohms	IEC 60093
体积电阻率 3	> 1.0E+15	ohms·cm	IEC 60093
介电强度 4	37	kV/mm	IEC 60243-1
介电常数			IEC 60250
100 Hz	4.30		IEC 60250
1 MHz	4.30		IEC 60250
耗散因数			IEC 60250
100 Hz	2.0E-3		IEC 60250
1 MHz	0.010		IEC 60250
漏电起痕指数	125	V	IEC 60112

可燃性	额定值	单位制	测试方法
UL 阻燃等级 (1.5 mm)	V-0		UL 94

注射	额定值	单位制
干燥温度	180	°C
干燥时间	6.0	hr
加工（熔体）温度	350 到 390	°C
模具温度	140 到 180	°C

挤出	额定值	单位制
干燥温度	180	°C
干燥时间	6.0	hr
熔体温度	350 到 390	°C
口模温度	140 到 180	°C