北化院PBT
 中国物性表查询网 >> COC >> COC 5013F-04物性表

COC 5013F-04物性表

分类: COC   出处:仁捷塑化  更新时间:2017-07-11   添加到收藏  

 

TOPAS® 5013F-04

环烯烃共聚物

 

Topas Advanced Polymers, Inc.

产品说明:

Product Description
TOPAS 5013F-04 is a high temperature film extrusion grade for blends. It is a high clarity amorp

hous resin with high flow, high stiffness, moisture barrier, chemical resistance, thermoformabilit

y and purity for food and healthcare applications. It is used in monolayer cast blends, and in co

extruded blends in both cast and blown processes, for a wide variety of film and sheet product

s requiring excellent optics in applications such as heat resistant blister, hot fill, and easy tear p

ackaging. If performance at elevated temperatures is not required, we also offer lower glass tra

nsition temperature (Tg) grades of TOPAS.

Selected Applications

  • Decorative film and sheet
  • General packaging
  • Food packaging
  • Blown film
  • Healthcare and food contact

Leading Attributes
  • Gloss, hardness, chemical resistance, forming
  • Easy or linear tear, heat resistance, hot fill, gloss
  • Not manufactured with BPA, phthalates, or halogens
  • High strength and high productivity
  • Broad regulatory compliance

Related Grades for Packaging and Film Extrusion
  • TOPAS 6013F-04 - high temperature grade with standard flow
  • 基本信息  
    特性
    • 纯度高
    • 防潮
    • 刚性,高
    • 高光
    • 高强度
    • 共聚物
    • 流动性高
    • 耐化学性良好
    • 清晰度,高
    • 食品接触的合规性
    • 无 BPA
    • 无定形的
    • 无卤
    用途
    • 包装
    • 薄膜
    • 混合
    • 片材
    • 食品包装
    • 医疗/护理用品
    机构评级
    • FDA FCN 405
    • 欧洲 10/1/2011 12:00:00 AM
    形式
    • 粒子
    加工方法
    • 薄膜挤出
    • 吹塑薄膜
    • 共挤薄膜
    • 流延薄膜
    • 热成型
    物理性能 额定值 单位制 测试方法
    密度 1.02 g/cm³ ISO 1183
    熔流率(熔体流动速率)     ISO 1133
        190°C/2.16 kg < 0.10 g/10 min ISO 1133
        230°C/2.16 kg 8.0 g/10 min ISO 1133
    溶化体积流率(MVR)     ISO 1133
        190°C/2.16 kg < 0.100 cm³/10min ISO 1133
        230°C/2.16 kg 9.00 cm³/10min ISO 1133
    吸水率 (饱和, 23°C) 0.010 % ISO 62
    薄膜 额定值 单位制 测试方法
    薄膜厚度 - 经测试 70 µm  
    拉伸模量     ISO 527-3/1
        MD : 70 µm, 铸造薄膜 2600 MPa ISO 527-3/1
        TD : 70 µm, 铸造薄膜 2500 MPa ISO 527-3/1
    拉伸应力     ISO 527-3/50
        MD : 断裂, 70 µm, 铸造薄膜 35.0 MPa ISO 527-3/50
        TD : 断裂, 70 µm, 铸造薄膜 25.0 MPa ISO 527-3/50
    伸长率     ISO 527-3/50
        MD : 断裂, 70 µm, 铸造薄膜 1.4 % ISO 527-3/50
        TD : 断裂, 70 µm, 铸造薄膜 1.1 % ISO 527-3/50
    落锤冲击 (70 µm, 铸造薄膜) < 36 g ISO 7765-1
    埃尔曼多夫抗撕强度     ISO 6383-2
        MD : 70 µm, 铸造薄膜 0.11 N ISO 6383-2
        TD : 70 µm, 铸造薄膜 0.11 N ISO 6383-2
    透氧率 (23°C, 70 µm, 挤塑薄膜, 50% RH) 26 cm³·mm/m²/atm/24 hr ASTM D3985
    水气透过率 (70 µm, 38°C, Cast Film, 90% RH) 0.14 g·mm/m²/atm/24 hr ASTM F1249
    热性能 额定值 单位制 测试方法
    玻璃转化温度 134 °C ISO 11357-2
    光学性能 额定值 单位制 测试方法
    光泽度 (60°, 70.0 µm, 铸造薄膜) > 100   ISO 2813
    雾度 (70.0 µm, 铸造薄膜) < 1.0 % ISO 14782
    挤出 额定值 单位制  
    挤塑机进料部分 20 到 70 °C  
    挤出机螺杆长径比L / D > 28:1    
    料筒1区温度 220 到 240 °C  
    料筒2区温度 220 到 240 °C  
    料筒3区温度 220 到 240 °C  
    料筒4区温度 220 到 240 °C  
    口模温度 220 到 240 °C

亲,如果要PDF物性表,可以到物性下载栏目下载,或发邮件到:tjh@rjplastics.com索取!